标题：Mechanical and Explosive Properties of Plastic Bonded Explosives Based on Mixture of HMX and TATB
本地全文：下载
作者：Arjun Singh ; Mahesh Kumar ; Pramod Soni 等
期刊名称：Defence Science Journal
印刷版ISSN：0976-464X
出版年度：2013
卷号：63
期号：6
页码：622-629
DOI：10.14429/dsj.63.5764
语种：English
出版社：Defence Scientific Information & Documentation Centre
摘要：This paper describes formulation of plastic bonded explosives (PBXs) compositions based on 2,4,6- triamino-1,3,5-trinitrobenzene (TATB), Octahydro l,3,5,7-tetranitro- 1,3,5,7-tetrazocine (HMX) by varying their relative amounts with Viton A as polymeric binder by slurry coating technique. These PBXs compositions are studied for mechanical and detonic properties. It has been observed that sensitivity and explosive performance of PBXs based on mixture of HMX and TATB were varied over a wide considerable range by varying relative amounts of TATB and HMX. The detonation study revealed there was increased in velocity of detonation (VOD) and detonation pressure with increasing amount of HMX from 10-80 % by weight. The sensitivity test results exhibited that insensitivity to impact for PBXs compositions was found to decrease with increasing HMX amount. Friction sensitivity study showed that no reactions were observed upto 36 kg load for PBXs compositions namely HT6030, HT5040, HT4050, HT3060, HT2070 and HT1080. The compressive strength of these PBXs compositions was found within the range of 9-11 MPa. Defence Science Journal, 2013, 63(6), pp.622 -629 , DOI:http://dx.doi.org/10.14429/dsj.63.5764
关键词：High explosive, plastic bonded explosive, detonic, sensitivity, mechanical property