文章基本信息

标题：Welding Studies on a Near-alpha Titanium Alloy
本地全文：下载
作者：Suresh Meshram ; T. Mohandas
期刊名称：Defence Science Journal
印刷版ISSN：0976-464X
出版年度：2011
卷号：61
期号：6
页码：590-596
DOI：10.14429/dsj.61.648
语种：English
出版社：Defence Scientific Information & Documentation Centre
摘要：The mechanical properties and microstructures of electron beam and friction welds of a near-alpha titanium alloy IMI 834 (presently TIMET 834) have been evaluated. Electron beam welds that contain micro pores and friction welds are free from such solidification-related defects. Porosity index in electron beam welds shows a decreasing trend with an increase in the welding speed. Electron beam welds contain coarse prior β grains and fine transformed β microstructure while, friction welds contain fine prior β grains and coarse transformed β microstructure. Electron beam welds with fine transformed β microstructure exhibited higher strength as compared to friction welds with coarse transformed β microstructure. The impact toughness of both the welds is comparable. Drastic reduction in impact toughness was observed when the welds were subjected to post-weld ageing as a result of inter-lath precipitation. Coarse-grained electron beam welds exhibited better creep and stress rupture properties as compared to friction welds. Defence Science Journal, 2011, 61(6), pp.590-596 , DOI:http://dx.doi.org/10.14429/dsj.61.648
关键词：Electron Beam weld;Friction weld;Mechanical and metallurgical properties