文章基本信息

标题：Experimental thermal hazard investigation on carbonate electrolytes using a cone calorimeter
本地全文：下载
作者：Que Huang ; Song Lu ; Xiaozhao Liu 等
期刊名称：Case Studies in Thermal Engineering
印刷版ISSN：2214-157X
电子版ISSN：2214-157X
出版年度：2021
卷号：25
页码：100912
DOI：10.1016/j.csite.2021.100912
出版社：Elsevier B.V.
摘要：During the thermal runaway (TR) processing of lithium-ion batteries (LIBs), electrolyte would release most of the heat as the main component. Thus, study on the fire risk of electrolyte is conductive to quantitatively evaluate the safety of LIBs. In this work, the combustion characteristics of three kinds of carbonate mixture electrolytes and the composition of residue were investigated. The significant parameters from the cone calorimeter tests reflecting the thermal hazards such as heat release rate (HRR), mass loss rate (MLR) and open cup flash point were measured. The HRR curves at the radiant power of 15 and 25 kW/m 2 were more gradual than those at 35 kW/m 2 which had one or two apparent peaks. The addition of diethyl carbonate (DEC) increased the HRRs significantly. The applicability of thermal chemistry (TC) theory used to calculate HRR in previous works was studied. The results of TC technique had a disparity with those from the cone calorimeter called oxygen consumption (OC) calorimetry especially for the electrolyte containing DEC, which was proved by thermogravimetry-Fourier transform infrared spectroscopy (TG-FTIR) experimental results, while it is different from the conclusion reported in previous study. The constituent of carbonate electrolytes residue was analyzed by the X-ray Fluorescence (XRF). Element fluorine (F) accounted for over 90% of the residue. The open cup flash point and ignition temperature were determined by the open cup flash point apparatus. The results showed that the fire point was very close to the open cup flash point, and the difference was within 0.1 K.
关键词：Lithium-ion batteries ; Electrolyte ; Cone calorimeter ; Heat release rate