标题：New Insights of Wear Behavior Analysis on Low Temperature Treated AISI 253MA Stainless steel Material by Gas Nitriding Process
本地全文：下载
作者：K. Ramya Sree ; G. Keerthi Reddy ; K. Aishwarya 等
期刊名称：E3S Web of Conferences
印刷版ISSN：2267-1242
电子版ISSN：2267-1242
出版年度：2020
卷号：184
页码：1-4
DOI：10.1051/e3sconf/202018401003
出版社：EDP Sciences
摘要：AISI 253MA Stainless steel samples were treat with the gas nitrating process at low heat around 4500C. It was seen that all-inclusive austenite stage exist when it is nitrade to 8 hours and post addition at time of nitrading to 16 hours the mix of ferrites and progressively substance of nitrogen was gathered in the following layers. Farther nitrading to 24 hour it has seen at Cr-N stage was discovered and turns the steel progressively firmer superficially. Erode tests were led by tribological wear testing machine to examine the tribological wear loss. Volume wear was found to be least in 18 hours test which demonstrated better improvement of wear improvement. High hardness were found in 24 hrs showing a hardness of 1080Hv. The sample nitrided to 24 hours exhibited better wear resistance, high hardness and low wear loss as well as low volume wear loss. Assessment examinations of nitrided test samples were investigated under scanning electron magnifying analysis.
其他摘要：AISI 253MA Stainless steel samples were treat with the gas nitrating process at low heat around 450°C. It was seen that all-inclusive austenite stage exist when it is nitrade to 8 hours and post addition at time of nitrading to 16 hours the mix of ferrites and progressively substance of nitrogen was gathered in the following layers. Farther nitrading to 24 hour it has seen at Cr-N stage was discovered and turns the steel progressively firmer superficially. Erode tests were led by tribological wear testing machine to examine the tribological wear loss. Volume wear was found to be least in 18 hours test which demonstrated better improvement of wear improvement. High hardness were found in 24 hrs showing a hardness of 1080Hv. The sample nitrided to 24 hours exhibited better wear resistance, high hardness and low wear loss as well as low volume wear loss. Assessment examinations of nitrided test samples were investigated under scanning electron magnifying analysis.