标题：FABRICATION OF A POROUS CARBON ELECTRODE PREPARED WITH CANDLENUT SHELL AND DESIGN OF CAPACITIVE DEIONIZATION (CDI) SYSTEM PROTOTYPE FOR DESALINATION OF BRAKISH WATER
其他标题：PEMBUATAN ELEKTRODA KARBON BERPORI DARI TEMPURUNG KEMIRI DAN PERANCANGAN PROTOTIPE SISTEM CAPACITIVE DEIONIZATION (CDI) UNTUK DESALINASI AIR PAYAU
本地全文：下载
作者：Astuti ; Astuti ; M. Taspika 等
期刊名称：Jurnal Pendidikan Fisika Indonesia
印刷版ISSN：1693-1246
电子版ISSN：2355-3812
出版年度：2015
卷号：11
期号：1
页码：100-107
DOI：10.15294/jpfi.v11i1.4008
语种：English
出版社：Semarang State University
摘要：A research on the activated carbon that prepared with the candlenut shell by using H3 PO4 2,5% as the activating agent has been done. All samples were heated at the temperatures of (400, 500, and 600) o C. The activated carbon have specific surface area (6.582; 95.623; and 391.567) m2 /g respectively. Capacitor electrode for capacitive deionization (CDI) was fabricated by using activated carbon that was heated at activation temperature of 600 o C with polyvinyl alcohol (PVA) as the binder. Based on cyclicvoltammogram of electrode, specific capacitance of CDI electrode is 50.21 mF/g. To observe desalination process of electrode, CDI was made by monopolar system and immersed in NaCl 0.24 M as brackish water sample. Direct current voltage 1.2 V was applied to CDI cell. The decrease of NaCl conductivity with CDI system respectively is 61.58%. Sodium concentration in NaCl decreases from 138.000 mg/L to 80.667 mg/L about 40 minutes of desalination process.The activated carbon that prepared from candlenut shell is potential to be developed as CDI system for desalination of brakish water.
其他摘要：Telah dilakukan pembuatan karbon aktif dengan bahan dasar tempurung kemiri menggunakan H3 PO4 2,5% sebagai aktivator dengan suhu aktivasi (400, 500, dan 600) o C.Luas permukaan aktif yang dihasilkan masingmasing adalah (6,6; 95,6; dan 391,6) m2 /g. Karbon
关键词：activated carbon; desalination; capacitive deionization (CDI)