摘要:A novel UV transparent conducting films based on Sb2O3/Ag/Sb2O3 (SAS) structure, which were prepared by an electron-beam thermal evaporation at room temperature. This SAS exhibits excellent electrical, optical and stable properties. Especially for UV region, the SAS has high transmittance of 80% at 306 nm and 92% at 335 nm, meanwhile achieving low sheet resistance ( ≤ 10 Ω sq(-1)). The UV OLED based on the SAS show competitive device performance. The UV OLED obtains the peak of UV electroluminescence at 376 nm and shows a very high maximum EQE of 4.1% with the maximum output power density of 5.18 mW cm(-2). These results indicate that the potential of SAS applications in deep UV transparent electrodes and large-scale flexible transparent electronics.