文章基本信息

标题：Location, location & size: defects close to surfaces dominate fatigue crack initiation
本地全文：下载
作者：Itziar Serrano-Munoz ; Jean-Yves Buffiere ; Rajmund Mokso 等
期刊名称：Scientific Reports
电子版ISSN：2045-2322
出版年度：2017
卷号：7
期号：1
DOI：10.1038/srep45239
语种：English
出版社：Springer Nature
摘要：Metallic cast components inevitably contain defects such as shrinkage cavities which are inherent to the solidification process. Those defects are known to significantly alter the fatigue life of components. Yet very little is known, quantitatively, on the dangerosity of internal casting defects compared to surface ones. In this study, fatigue specimens containing controlled internal defects (shrinkage pores) are used to foster internal cracking. In situ fatigue tests monitored by X ray synchrotron tomography revealed that the internal nucleation and propagation of cracks was systematically overran by surface cracking initiated at castings defects up to ten times smaller than the internal ones. These findings indicate that the presence of internal defects in cast components can be tolerated to a larger extent than is allowed by nowadays standards.