标题：Real internal microstructure based key mechanism analysis on the micro-damage process of short fibre-reinforced composites
本地全文：下载
作者：Xiaofang Hu ; Jian Fang ; Feng Xu 等
期刊名称：Scientific Reports
电子版ISSN：2045-2322
出版年度：2016
卷号：6
期号：1
DOI：10.1038/srep34761
语种：English
出版社：Springer Nature
摘要：In this work, the underlying micro-damage mechanisms of randomly oriented short fibre-reinforced composites were revealed based on real internal microstructural characteristics obtained by high-resolution (0.7 μm/pixel) synchrotron radiation X-ray computed tomography (SR-CT). The special 'pore dominant micro-damage processes' were directly observed through SR-CT three-dimensional reconstructed images, which were different from the well-known 'fibre breakage dominant failure mode'. The mechanisms of pore formation and pore evolution were further investigated on the basis of the microstructural parameters extracted from the SR-CT results. On one hand, the pore formation mechanism caused by shear stress concentration was proposed by combining the shear-lag model with the microstructural parameters obtained from the experiment, including the fibre length and orientation angle. On the other hand, the 'fibre-end aggregation-induced pore connection' mode of crack initiation was proposed through a composites model, which considered the parameters of real internal microstructure, including the critical value of the distance between neighbouring fibre ends and the number of neighbouring fibre ends. The study indicated that the shear stress concentration was significant in the region with a large number of neighbouring fibre ends, thus causing pore connection and crack initiation.