文章基本信息

标题：The Adsorption of Copper by SBA-15-CPTMS Mesoporous for Water Remediation
本地全文：下载
作者：Donanta Dhaneswara ; Farhan Delayori ; Siti Utami 等
期刊名称：E3S Web of Conferences
印刷版ISSN：2267-1242
电子版ISSN：2267-1242
出版年度：2018
卷号：65
页码：1-10
DOI：10.1051/e3sconf/20186505007
出版社：EDP Sciences
摘要：The high development of science and technology affects the economic growth and industrialization process. The industrialization process produces industrial waste which contain heavy metal such as copper (Cu). This industrial waste can harm the environment surronding industrial areas where 15 million or 6% of the Indonesian population live. In order to overcome this problem, mesoporous silica material Santa Barbara Amorphous-15 (SBA-15) is used as an adsorbent. SBA-15 was synthesized through sol gel process using tetraorthosilicate as precursor, Pluronic 123 triblock copolymer as template, and (3-chloropropyl)trimethoxysilane (CPTMS) as functionalized agent. CPTMS was used to modify the SBA-15 surface in order to improve the materials as adsorbent. The materials were characterized using SAXRD and TEM to study material’s cristallinity and pore structure, the presence of organic group was examined using FTIR, the surface area of SBA-15 and SBA-15 CPTMS were characterized using Brunauer Emmett Teller (BET) N2 adsorption isotherm test at 77 K, and the ions concentration in solution after adsorption process was determined using AAS. The crystal structure of SBA-15 and SBA-15 CPTMS was found 2D heksagonal with a more regular SBA-15 pore structure than SBA-15 CPTMS. The surface area of SBA-15-CPTMS was found to be lower than SBA-15, 711.061 m2/g in comparison to 831.996 m2/g. However, in copper adsorption test, it was found that SBA-15-CPTMS has higher adsorption ability.
其他摘要：The high development of science and technology affects the economic growth and industrialization process. The industrialization process produces industrial waste which contain heavy metal such as copper (Cu). This industrial waste can harm the environment surronding industrial areas where 15 million or 6% of the Indonesian population live. In order to overcome this problem, mesoporous silica material Santa Barbara Amorphous-15 (SBA-15) is used as an adsorbent. SBA-15 was synthesized through sol gel process using tetraorthosilicate as precursor, Pluronic 123 triblock copolymer as template, and (3-chloropropyl)trimethoxysilane (CPTMS) as functionalized agent. CPTMS was used to modify the SBA-15 surface in order to improve the materials as adsorbent. The materials were characterized using SAXRD and TEM to study material’s cristallinity and pore structure, the presence of organic group was examined using FTIR, the surface area of SBA-15 and SBA-15 CPTMS were characterized using Brunauer Emmett Teller (BET) N₂ adsorption isotherm test at 77 K, and the ions concentration in solution after adsorption process was determined using AAS. The crystal structure of SBA-15 and SBA-15 CPTMS was found 2D heksagonal with a more regular SBA-15 pore structure than SBA-15 CPTMS. The surface area of SBA-15-CPTMS was found to be lower than SBA-15, 711.061 m2/g in comparison to 831.996 m²/g. However, in copper adsorption test, it was found that SBA-15-CPTMS has higher adsorption ability.