标题：Utilization of crown pineapple waste as raw material preparation of activated carbon as adsorbent in natural gas storage
本地全文：下载
作者：Yuliusman ; Nasruddin ; H I Naf’an 等
期刊名称：E3S Web of Conferences
印刷版ISSN：2267-1242
电子版ISSN：2267-1242
出版年度：2018
卷号：67
页码：1-4
DOI：10.1051/e3sconf/20186702018
出版社：EDP Sciences
摘要：Activated carbon used as natural gas storage in adsorbed natural gas technology due to physical adsorption properties. Pineapple crown was used as raw material for activated carbon by reason of high lignocellulose content. The purpose of this study is to produce high surface area of activated carbon with high carbon composition (up to 80% weight). Activated carbon were prepared through chemical activation using KOH with various weight ratio and physical activation using N2 with 150 ml/min flowrate. Carbonization of pineapple crown is done at 350°C followed by chemical activation with KOH activator and physical activation. The result of iod number indicate the 1:1 weight KOH ratio gave the highest iod number 1337 mg/mg and 1190.799 m2/g surface area achieved by chemical-physical activation.
其他摘要：Activated carbon used as natural gas storage in adsorbed natural gas technology due to physical adsorption properties. Pineapple crown was used as raw material for activated carbon by reason of high lignocellulose content. The purpose of this study is to produce high surface area of activated carbon with high carbon composition (up to 80% weight). Activated carbon were prepared through chemical activation using KOH with various weight ratio and physical activation using N2 with 150 ml/min flowrate. Carbonization of pineapple crown is done at 350°C followed by chemical activation with KOH activator and physical activation. The result of iod number indicate the 1:1 weight KOH ratio gave the highest iod number 1337 mg/mg and 1190.799 m²/g surface area achieved by chemical-physical activation.