文章基本信息

标题：Properties of recycled ceramic aggregates specified in WT-1 2014 Aggregates - Technical Requirements
本地全文：下载
作者：Wojciech Andrzejuk ; Mateusz Sałuch ; Bartosz Zegardło 等
期刊名称：E3S Web of Conferences
印刷版ISSN：2267-1242
电子版ISSN：2267-1242
出版年度：2018
卷号：49
页码：1-6
DOI：10.1051/e3sconf/20184900001
出版社：EDP Sciences
摘要：The article presents the results of research on primary recycling properties of ceramic aggregates conducted following the procedures outlined in WT-1 2014 Aggregates − Technical Requirements. The material for the tests was obtained from a company producing sanitary ceramic products. Damaged ceramic products, coming from the factory waste heaps, were transported to the laboratory and crushed. This enabled producing aggregate that was later subjected to tests carried out on the aggregates commonly used in the production of mineral-asphalt mixes applied in making road surfaces. The factors that were examined include the following: the flow rate of fine aggregates (angularity of fine aggregate), fine particles content - methylene blue test, light-weight impurities content, frost resistance, bulk density of grains as well as water absorption determined by pycnometric method. The test results showed that the properties of the recycled aggregates are similar to those included in traditional aggregates used for the production of mineral-asphalt mixes. On the basis of the conducted analyses, the waste ceramic aggregate was recommended for use.
其他摘要：The article presents the results of research on primary recycling properties of ceramic aggregates conducted following the procedures outlined in WT-1 2014 Aggregates - Technical Requirements. The material for the tests was obtained from a company producing sanitary ceramic products. Damaged ceramic products, coming from the factory waste heaps, were transported to the laboratory and crushed. This enabled producing aggregate that was later subjected to tests carried out on the aggregates commonly used in the production of mineral-asphalt mixes applied in making road surfaces. The factors that were examined include the following: the flow rate of fine aggregates (angularity of fine aggregate), fine particles content - methylene blue test, light-weight impurities content, frost resistance, bulk density of grains as well as water absorption determined by pycnometric method. The test results showed that the properties of the recycled aggregates are similar to those included in traditional aggregates used for the production of mineral-asphalt mixes. On the basis of the conducted analyses, the waste ceramic aggregate was recommended for use.