文章基本信息

标题：Strength and Microstructure of Concrete with Iron Ore Tailings as Replacement for River Sand
本地全文：下载
作者：Ali Umara Shettima ; Yusof Ahmad ; Mohd Warid Hussin 等
期刊名称：E3S Web of Conferences
印刷版ISSN：2267-1242
电子版ISSN：2267-1242
出版年度：2018
卷号：34
页码：1-9
DOI：10.1051/e3sconf/20183401003
出版社：EDP Sciences
摘要：River Sand is one of the basic ingredients used in the production of concrete. Consequently, continuous consumption of sand in construction industry contributes significantly to depletion of natural resources. To achieve more sustainable construction materials, this paper reports the use of iron ore tailings (IOT) as replacement for river sand in concrete production. IOT is a waste product generated from the production of iron ore and disposed to land fill without any economic value. Concrete mixtures containing different amount of IOT were designed for grade C30 with water to cement ratio of 0.60. The percentage ratios of the river sand replacements by IOT were 25%, 50%, 75% and 100%. Concrete microstructure test namely, XRD and Field Emission Scanned Electron Microscopic/Energy dispersive X-ray Spectroscopy (FESEM/EDX) were conducted for control and IOT concretes in order to determine the interaction and performance of the concrete containing IOT. Test results indicated that the slump values of 130 mm and 80 to 110 mm were recorded for the control and IOT concretes respectively. The concrete sample of 50% IOT recorded the highest compressive strength of 37.7 MPa at 28 days, and the highest flexural strength of 5.5 MPa compared to 4.7 MPa for reference concrete. The texture of the IOT is rough and angular which was able to improve the strength of the concrete.