标题：High-capacity, low-tortuosity, and channel-guided lithium metal anode
本地全文：下载
作者：Ying Zhang ; Wei Luo ; Chengwei Wang 等
期刊名称：Proceedings of the National Academy of Sciences
印刷版ISSN：0027-8424
电子版ISSN：1091-6490
出版年度：2017
卷号：114
期号：14
页码：3584-3589
DOI：10.1073/pnas.1618871114
语种：English
出版社：The National Academy of Sciences of the United States of America
摘要：Lithium metal anode with the highest capacity and lowest anode potential is extremely attractive to battery technologies, but infinite volume change during the Li stripping/plating process results in cracks and fractures of the solid electrolyte interphase, low Coulombic efficiency, and dendritic growth of Li. Here, we use a carbonized wood (C-wood) as a 3D, highly porous (73% porosity) conductive framework with well-aligned channels as Li host material. We discovered that molten Li metal can infuse into the straight channels of C-wood to form a Li/C-wood electrode after surface treatment. The C-wood channels function as excellent guides in which the Li stripping/plating process can take place and effectively confine the volume change that occurs. Moreover, the local current density can be minimized due to the 3D C-wood framework. Therefore, in symmetric cells, the as-prepared Li/C-wood electrode presents a lower overpotential (90 mV at 3 mA⋅cm⁻²), more-stable stripping/plating profiles, and better cycling performance (∼150 h at 3 mA⋅cm⁻²) compared with bare Li metal electrode. Our findings may open up a solution for fabricating stable Li metal anode, which further facilitates future application of high-energy-density Li metal batteries.
关键词：lithium metal batteries ; wood channels ; low tortuosity ; stable cycling ; high capacity