期刊名称：Proceedings of the National Academy of Sciences
印刷版ISSN：0027-8424
电子版ISSN：1091-6490
出版年度：2016
卷号：113
期号：37
页码：10257-10262
DOI：10.1073/pnas.1610920113
语种：English
出版社：The National Academy of Sciences of the United States of America
摘要：Owing to their glassy nature, metallic glasses demonstrate a toughness that is extremely sensitive to the frozen-in configurational state. This sensitivity gives rise to “annealing embrittlement,” which is often severe and in many respects limits the technological advancement of these materials. Here, equilibrium configurations (i.e., “inherent states”) of a metallic glass are established around the glass transition, and the configurational properties along with the plane-strain fracture toughness are evaluated to associate the intrinsic glass toughness with the inherent state properties and identify the fundamental origin of embrittlement. The established correlations reveal a one-to-one correspondence between toughness and shear modulus continuous over a broad range of inherent states, suggesting that annealing embrittlement is controlled almost solely by an increasing resistance to shear flow. This annealing embrittlement sensitivity is shown to vary substantially between metallic glass compositions, and appears to correlate well with the fragility of the metallic glass.
关键词：ductility ; amorphous metal ; fracture toughness
Loading...