文章基本信息

标题：Structural, Optical and Photoconductive Properties of Brush Plated Copper Gallium Selenide films
本地全文：下载
作者：N. P. Subiramaniyam ; P. Thirunavukkarasu ; K. R. Murali 等
期刊名称：Journal of Environmental Nanotechnology
印刷版ISSN：2279-0748
电子版ISSN：2319-5541
出版年度：2013
卷号：2
期号：1
页码：63-70
语种：English
出版社：Institute for Environmental Nanotechnology
摘要：Copper Gallium selenide films were deposited for the first time by the brush electrodeposition technique. The films were deposited at different bath temperatures in the range of 30 - 80°C at a constant current density of 3.0 mA cm-2. The films exhibited single phase Copper Gallium selenide. Optical band gap of the film deposited at 80°C was1.68 eV. Room temperature resistivity of the films were in the range of 0.1 - 14.0 ohm cm. Photoconductivity measurements were made at room temperature. Photocurrent Capacitance voltage measurements indicated the films to exhibit p -type behaviour. The flat band potential (Vfb) was 0.60V (SCE) and a carrier density in the range of 2.5 x 1017 cm-3 was obtained. A single Photoluminescence peak was observed at 1.64 eV. Keywords: Chalcopyrite; I-III-VI2; Ssemiconductors; Thin films.