标题：Low temperature solution process-based defect-induced orange-red light emitting diode
本地全文：下载
作者：Pranab Biswas ; Sung-Doo Baek ; Sang Hoon Lee 等
期刊名称：Scientific Reports
电子版ISSN：2045-2322
出版年度：2015
卷号：5
DOI：10.1038/srep17961
出版社：Springer Nature
摘要：We report low-temperature solution-processed p-CuO nanorods (NRs)/n-ZnO NRs heterojunction light emitting diode (LED), exploiting the native point defects of ZnO NRs. ZnO NRs were synthesized at 90 °C by using hydrothermal method while CuO NRs were synthesized at 100 °C by using microwave reaction system. The electrical properties of newly synthesized CuO NRs revealed a promising p-type nature with a hole concentration of 9.64 × 10¹⁸ cm⁻³. The current-voltage characteristic of the heterojunction showed a significantly high rectification ratio of 10⁵ at 4 V with a stable current flow. A broad orange-red emission was obtained from the forward biased LED with a major peak at 610 nm which was attributed to the electron transition from interstitial zinc to interstitial oxygen point defects in ZnO. A minor shoulder peak was also observed at 710 nm, corresponding to red emission which was ascribed to the transition from conduction band of ZnO to oxygen vacancies in ZnO lattice. This study demonstrates a significant progress toward oxide materials based, defect-induced light emitting device with low-cost, low-temperature methods.