标题：Prototype Profile of Supercapactors with Activated Carbon/Fe3O4 Electrodes Natural Materials and Celgard Li-Ion Battery Separators
本地全文：下载
作者：Lydia Rohmawati ; Damini Alfarisi ; Sitiv Holisa SP 等
期刊名称：E3S Web of Conferences
印刷版ISSN：2267-1242
电子版ISSN：2267-1242
出版年度：2021
卷号：328
页码：1-5
DOI：10.1051/e3sconf/202132802012
语种：English
出版社：EDP Sciences
摘要：The electrode composition material in the supercapacitor affects the storage performance of the supercapacitor. In this study, the electrodes were made from coconut shell activated carbon and Fe3O4 from iron sand. To be used as electrodes, the two materials are mixed with PVDF and a solution of Dimethylacetamide at a temperature of 70°C; then, a coating process is carried out by layering the electrode material onto aluminium foil to obtain an electrode sheet. The coin cell assembling process was then carried out by arranging the electrode sheets and the Celgard Li-ion battery separator in the glove box and then tested for charge/discharge with a current density of 5-81 mA/g and cycle stability at a current of 20 mA/g. The study results show that the activated carbon/5 wt% Fe3O4 supercapacitor has the best capacitance value for charging at 8.03 F/g and discharging at 8.55 F/g at a current density of 5 mA/g. The activated carbon/5 wt% Fe3O4 supercapacitor has cycle stability of up to 200 cycles and can withstand up to 95% with a capacitance of 6.6 F/g.
关键词：Activated carbon/Fe3O4;Electrode;Supercapacitor