标题：Study of effectiveness of heavy metals ions as the inhibitors of steel corrosion
本地全文：下载
作者：Tatiana Shabliy ; Julia Nosachova ; Yaroslav Radovenchik 等
期刊名称：Eastern-European Journal of Enterprise Technologies
印刷版ISSN：1729-3774
电子版ISSN：1729-4061
出版年度：2017
卷号：4
期号：12
页码：10-17
DOI：10.15587/1729-4061.2017.106974
语种：English
出版社：PC Technology Center
摘要：The effect of ions of d-metals on the processes of corrosion in a movable and immovable neutral aqueous environment has been investigated. It was shown that a number of ions, such as zinc, chromium, lead, under conditions of high aeration and temperature of 20 ºС at concentrations of 2−5 mg/dm3, are effective inhibitors of steel corrosion. This is due to the formation of a passivation oxygen film on the surface of metal. The degree of corrosion protection is maintained at the level of 80−90 %. In the case of elevating the temperature to 50 ºС, a significant (up to 40 %) decrease in the inhibitory properties of ions of d-metals is observed. This is due both to the destabilization of the oxygen passivation film and the growth of oxidation rate of steel with increasing temperature.It was demonstrated that phosphonic acids, such as oxyethyldidiphosphone acid, nitrilotrimethylphosphonium acid, due to the interaction of complexons with the surface of metals, stabilize the passivation oxygen film, providing a degree of protection against corrosion at 95−98 % at acid dose of 10 mg/dm3. However, when the temperature rises to 50 °C, a protective effect is reduced.It was established that the use of compositions based on OEDPhA/NTMPhA and Zn/Pb/Cr ions in the range of temperatures 20−50 oC provides a degree of protection of steel from corrosion at the level of 90 %. This is explained by the formation of three-dimensional complexes of phosphonic acids with metal ions and corroded iron
关键词：corrosion;inhibitors;heavy metals;stabilizers of scale formation;closed water-circulation systems