文章基本信息

标题：Corrosion behavior of HRB400 and HRB400M steel bars in concrete under DC interference
本地全文：下载
作者：Qingmiao Ding ; Yuning Gao ; Ruiyang Liu 等
期刊名称：Scientific Reports
电子版ISSN：2045-2322
出版年度：2021
卷号：11
DOI：10.1038/s41598-021-03412-7
语种：English
出版社：Springer Nature
摘要：The influence of direct current interference on the corrosion behavior of HRB400 and HRB400M steel bars in simulated concrete solution was studied using methods such as weight loss experiment, electrochemical experiment, surface technology and product analysis. The research results showed that with the increase of DC interference voltage, the corrosion rates of HRB400 and HRB400M steel bars would increase. The corrosion resistance of HRB400M steel bars was better than HRB400 steel bars under the experimental conditions. In addition, direct current interference could cause damage to the corrosion product layer on the surface of HRB400 steel bars and HRB400M steel bars. And the corrosion form and corrosion product types of HRB400 and HRB400M steel bars would be affected by direct current interference. The main corrosion products of HRB400 steel bars included γ-FeOOH and Fe 2O 3 when it was not interfered by DC. When DC interference was applied, the main corrosion products included Fe 3O 4 and Fe 2O 3. The corrosion products on the surface of HRB400M steel bars were mainly Fe 3O 4 and Fe 2O 3, and the types of products increased to form Cr 2O 3 and MnFe 2O 4.