标题：Prevent Cracking in Deposition of Carbon Steel on Inconel 625
本地全文：下载
作者：M. A. Morsy ; M. R. El Koussy ; M. M. Farag 等
期刊名称：MATEC Web of Conferences
电子版ISSN：2261-236X
出版年度：2019
卷号：269
DOI：10.1051/matecconf/201926903011
语种：English
出版社：EDP Sciences
摘要：Welding procedure of clad steel including deposition of carbon steel on nickel base alloy usually gives unaccepted mechanical properties. Cracks were formed along type II boundary in nickel base alloy pass and a martensitic layer was formed in carbon steel pass. In this paper, cracks along type II boundary were prevented by lowering the martensitic start temperature (TMs) of the martensitic layer. Decreasing of TMswas obtained by two methods:Dilution methodandGrain refining method. Three levels of TMs(approximately 350, 200, and 50⁰C) are obtained. The results showed that: cracks along type II boundary were prevented at TMslower than 200⁰C; however type II boundary itself was prevented at TMslower than 50??. Also post weld heat treatment was necessary to achieve accepted impact properties.