文章基本信息

标题：Preparation of water-soluble asphalt carbon dots and hyperchromic effect to Cr (VI)
本地全文：下载
作者：Lijuan Gao ; Jia Sui ; Xiaoqin Qiao 等
期刊名称：MATEC Web of Conferences
电子版ISSN：2261-236X
出版年度：2018
卷号：238
DOI：10.1051/matecconf/201823802007
语种：English
出版社：EDP Sciences
摘要：Water-soluble asphalt carbon dots (W-CDs) was prepared from medium - temperature coal tar pitch as raw material, via mixed acid oxidation, alkali solubilization and acid precipitation method. It was observed that as-prepared W-CDs were irregular particles with good water dispersibility and the particle size was controlled by the pH of the acid precipitation solution by a polarizing microscope. Infrared spectroscopy confirmed that the surface of the W-CDs was functionalized by hydrophilic and color-promoting functional groups, which had good water solubility; the thermal weight loss proved to be good thermal stability below 200°C; the fluorescence spectrum proved that the fluorescence emission peak position of the carbon dots appears red shift with increase of excitation wavelength, with fluorescence conversion property, and its emission light intensity decreases, belonging to non-resonant fluorescence type of direct jump fluorescence; UV spectrum proves that the addition of W-CDs can be chromium (VI) CrO42-content The detection limit was increased from milligram to microgram; the molar absorptivity of CrO42-was increased by 4 times. The experimentally optimized W-CDs-ultraviolet-viscometry method for measuring CrO42-conditions: W-CDs to chromium ratio of 8:2, pH of 8, hexamethylenetetramine as a surfactant, and the solution was allowed to stand at room temperature for 45 min.