标题：PRELIMINARY STUDIES OF RIVETED JOINTS AT FEED FORCE
本地全文：下载
作者：Radosław Bielawski ; Radosław Bielawski ; Michał Kowalik 等
期刊名称：Advances in Science and Technology Research Journal
印刷版ISSN：2080-4075
电子版ISSN：2299-8624
出版年度：2015
卷号：9
期号：27
页码：23-27
DOI：10.12913/22998624/59080
语种：English
出版社：Society of Polish Mechanical Engineers and Technicians
摘要：The aim of the study was to determine the feasibility of riveted joints in composites materials. Static tensile test method was used. In the test one type of glass fabric was used (Interglas 92140) from which two types of composite samples were prepared. In each sample the same type of fiber with the same fiber orientation – 3 layers - was used. The samples had dimensions of 100×100 mm and thickness of approximately 1 mm. The composite probes were located in a metal frame with a screw connection which was made of screws with nominal thread pitch M5. Screws were tightened with constant torque. It was to provide an axial force to the sample during the tensile test. The frame was placed between cross-bars of tensile machine INSTRON 8516. The samples were stretched at a speed of 0.05 mm/s at a distance up to 16 mm. During the tensile test displacement of the samples and pull force were registered. Depending on the fibre orientations and the value of feed force, damage models were described. On the basis of the results the possibility of usage of aluminium rivet nuts connections in composite materials was determined.
关键词：laminates;damage mechanics;mechanical testing;joints/joining