标题：Transient liquid phase bonding of magnesium alloys AZ31 using nickel coatings and high frequency induction heat sintering
本地全文：下载
作者：A.N. AlHazaa ; A.N. AlHazaa ; Khalil Abdelrazek Khalil 等
期刊名称：Journal of King Saud University - Science
印刷版ISSN：1018-3647
出版年度：2016
卷号：28
期号：2
页码：152-159
DOI：10.1016/j.jksus.2015.09.006
语种：English
出版社：Elsevier
摘要：Abstract Transient liquid phase (TLP) bonding process was applied to join magnesium alloy AZ31 samples with minimum microstructural changes. The magnesium samples were coated by 5μm nickel prior to the TLP bonding. Bonding conditions of 8MPa uniaxial pressure and 520°C bonding temperature were applied for all bonds at various bonding times. The microstructure across the joint regions was examined as a function of bonding time (5–60min). Investigating the change in Ni contents was examined by EDS line scan. It was noticed that Ni coating could not be observed by SEM for bonds made at 30 and 60min due to complete dissolution of the Ni coating. Second phase particles containing Mg2Ni intermetallics were observed by X-ray Photoelectron Spectroscopy (XPS) near the joint region. The shear strength of the bonds initially increases with the increase in bonding time till 20min. On the other hand, with bonding times over 20min the shear strength decreases. Therefore the optimum bonding time at the conditions applied was concluded to be 20min.
关键词：TLP bonding; Mg alloy; Coatings; Induction heating;